Customization: | Available |
---|---|
Color: | All Colors |
Appearance: | Liquid |
Still deciding? Get samples of US$ 0.01/Piece
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Mixing Ratio | Solid Colors | Hardener | Thinner |
(Volume) | 2 | 1 | |
<18°C | Solid Colors | ||
18-30°C | Solid Colors | ||
>30°C | Solid Colors |
Temperature | Dust Time | Dry to Handle | Thorough Dry |
25 °C | 40 minutes | 8 hours | 7 days |
70 °C | 5 minutes | 20 minutes | 60 minutes |
Surface Cleaning: Remove wax,silcon and other contaminations with degreaser. Mixing RatioBasecoat ColorsThinner |
|
Mixing ratio | 10.6-0.8 <15°C 1K Plain 15-30°C 1K Plain >30°C 1K Plain |
Spray Gun &Pressure: |
Gravity Feed 1.2-1.5mm 2-4kg/cm2 Siphon Feed 1.4-1.7mm 2-4kg/cm2 |
No.of Coats: | 2-3 coats. |
Flash-off time between coats: |
15-20 minutes . |
Recommended film thickness: | 15-25um |
Re-coat: | Re-coat with clearcoat. |
Characteristic: Double pack acrylic extra fast drying clear coat, easy application, good gloss, suitable for metal, solid basecoat and spot repair. Substrates: 1K Plain |
|||||
Surface Cleaning: | Clean the dust and particles with tack cloth | ||||
Mixing Ratio | |||||
Clear Coat | Hardener | ||||
2 | 1 | ||||
<18°C | |||||
18-30°C | |||||
>30°C | |||||
Pot-Life at 25°C | |||||
The mixture should be used up within 1 hour | |||||
Spray Gun Set-up | |||||
Gravity Feed | 1.2-1.5mm 3-5kg/cm2 |
Suction Feed | 1.4-1.7mm 3-5kg/cm2 |
||
Conventional | 3-4 bar | RP | 2.0-2.5 bar | ||
HVLP | 2.0 bar | ||||
Coats & Thickness | |||||
2-3 coats, tatal 50-70 um | |||||
Flash-off Time | |||||
At 20°C, 5-10 minutes between coats | |||||
Air-drying Time | |||||
Allow 15-20 minutes air drying time before force drying | |||||
Drying Time | |||||
Temperature | Dust Free | Dry to Handle | Dry to Polish | ||
20°C | 30-40 minutes | 120 minutes | 6 days | ||
15°C | 20-30 minutes | 60 minutes | 6 days | ||
25°C | 15-20 minutes | 40 minutes | 6 days | ||
60°C | 5 minutes | 10 minutes | 80 minutes |